发表刊物：High Temperature Materials and Processes
期号：1
卷号：43
影响因子：1.6
DOI码：10.1515/htmp-2024-0018
所属单位：东北大学冶金学院
教研室：绿色智能特殊钢冶金研究中心
摘要：Three parts of the experiment were mainly carried out in this research: the effect of Ca on inclusions in 38CrMoAl high aluminum steel under atmospheric pressure, the effect of pressure on the solubility of Ca in pure iron under pressurized conditions, and the effect of Ca on inclusions in 38CrMoAl high aluminum steel under pressurized conditions. The results indicated that Ca can significantly transform the inclusions such as Al2O3 and MgOAl2O3 with high melting points into calcium aluminate inclusions with low melting points. It was found that the pressure condition can significantly improve the solubility of Ca in pure iron and molten steel, which provided reliable data reference and guidance for popularizing Ca treatment of steel under pressure conditions in the future. Finally, the mechanism of inclusion transformation after Ca treatment was put forward. In this study, the theoretical calculation of thermodynamics was closely compared with the experimental data. It was proposed that to modify the inclusions in high aluminum steel into calcium aluminate inclusions with low melting points, it is necessary to accurately control Ca in the target region.
关键字：Ca treatment38CrMoAl steelinclusionshigh aluminum steelpressure steelmaking
论文类型：SCI
备注：无
学科门类：工学
一级学科：冶金工程
页面范围：20240018
ISSN号：0334-6455
是否译文：否