第一作者：杨皓
通讯作者：李阳
合写作者：夏铃,陈常勇,姜周华,李文宇,陈浩嘉
发表刊物：Journal of Materials Research and Technology
卷号：29
影响因子：6.2
DOI码：10.1016/j.jmrt.2024.01.251
所属单位：东北大学冶金学院
教研室：绿色智能特殊钢冶金研究中心
摘要：In order to solve the problem of forming liquid precipitated NbC when Nb is added excessively in high carbon steel. This study proposed to introduce Ce to form Ce-containing inclusions to inhibit the growth of large liquid precipitated NbC. The results show that in the high strength valve spring steel with 0.63 % carbon mass fraction, the large liquid precipitated NbC will be formed only if the mass fraction of Nb exceeds 0.0192 %. When the mass fraction of Ce in steel is higher than 0.0364 %. In addition to the formation of high melting point Ce2O3, Ce2C3 carbide will be precipitated at the end of solidification. And the amount of Ce2C3 precipitation will increase with the increase of Ce mass fraction in steel. Ce2O3 and Ce2C3 have low two-dimensional lattice mismatch degree with NbC. both of them can be nucleation sites of NbC, which lead to multi-point precipitation and avoid aggregation and growth of NbC. However, the content of Ce should not be too high, which will be dominated by the precipitation of Ce, and the best mass fraction of Ce and Nb is between 0.02 % and 0.05 %.
关键字：CeNbC65Si2CrVSpring steel
论文类型：SCI
备注：无
学科门类：工学
一级学科：冶金工程
页面范围：2239-2247
ISSN号：2238-7854
是否译文：否