摘要：The individual effect of Ca-containing ferrosilicon, MgO crucible, and slag-steel refining on the formation of endogenous CaO-containing inclusion in steel is investigated by contrast experiments. Experiments using Ca-containing ferrosilicon are compared with the effect of high basicity slag and MgO crucible on inclusions compared to experiments with high purity Si. It is found that the influence of Ca-containing ferrosilicon has a noticeable impact on endogenous CaO-containing, while slag-steel reaction and MgO refractory mainly increase the (MgO) in inclusion. When Ca-containing ferrosilicon is added after Al deoxidation, Al2O3 and MgO-xAl(2)O(3) inclusions with low MgO content are modified into CaO-containing inclusions preferentially, and [Mg] supplied by MgO refractory reacts mainly with (Al2O3) in inclusions in the subsequent refining process. Ca-containing ferrosilicon addition before Al deoxidation is helpful in reducing Ca content in the steel. The dissolution of refractory in slag has a significant effect on slag-steel reaction by changing slag composition. Under the effect of slag and MgO refractory, MgO-saturated spinel and MgO form in steel during the whole process. Herein, Ca-containing ferrosilicon is a significant contributor to endogenous CaO-containing inclusions during the simulated ladle furnace refining process without Ca treatment.
关键字：Ca-containing ferrosiliconCaO-containing inclusioninclusion transformationrefractoryslag-steel reactions
论文类型：SCI
备注：无
学科门类：工学
一级学科：冶金工程
页面范围：2200097
ISSN号：1611-3683
是否译文：否