第一作者：李阳
通讯作者：李花兵
合写作者：陈常勇,姜周华,孙萌,胡浩
发表刊物：ISIJ International
期号：7
卷号：58
影响因子：1.6
DOI码：10.2355/isijinternational.ISIJINT-2018-048
所属单位：东北大学冶金学院
教研室：绿色智能特殊钢冶金研究中心
摘要：A novel LF refining slag contains K2O has been developed in order to produce ultraclean saw wire steels. The diameter of ultrafine saw wire is between 50×10−6 m (50 µm) and 80 ×10−6 m (80 µm), any hard inclusion which diameter more than 5×10−6 m (5 µm) should be avoided because it probably will cause wire breaking. In order to enhance inclusion removal in C96V saw wire steel during LF refining process, fundamental work on the effect of alkali oxides (Li2O, K2O) on the absorption ability of inclusions in a typical LF refining slag for C96V saw wire steel has been investigated. The results indicated that K2O additions seems to significantly enhance inclusion removal in steel melts, instead, Li2O additions hindered inclusion removal. In details, K2O improve the cleanliness in the as quenched C96V saw wire steel melts compared to preexisting synthetic LF refining slag compositions: (i) The average diameter of nonmetallic inclusions was decreased sharply with the content of K2O in synthetic LF refining slag increasing. In particular, the diameter of most of inclusions was less than 2.5×10−6 m (2.5 µm) when the content of K2O in synthetic LF refining slag more than 10 wt%; (ii) The number of inclusions descend sharply with the content of K2O in synthetic LF refining slag raising. (iii) Both of the SiO2–MnO–Al2O3, SiO2–CaO–Al2O3 inclusions system mainly concentrated in the low melting zone when the composition of K2O in synthetic refining slag was less than 10 wt%. While the Li2O additions has the opposite effect.
关键字：C96V saw wire steels, LF refining slag, alkali oxides, inclusions
论文类型：SCI
备注：无
学科门类：工学
一级学科：冶金工程
页面范围：1232-1241
ISSN号：1347-5460
是否译文：否