第一作者：Zhang Zicheng

发表刊物：Advanced Materials Research

卷号：652-654

DOI码：10.4028/www.scientific.net/AMR.652-654.1956

摘要：In this study a cyclic rotating bending process for microstructure control of metal tubes was newly proposed. The AZ31 magnesium alloy tube was conducted to investigate the effect of the rotating bending process on the microstructure and mechanical properties of metal tubes. The rotating bending process was carried out with rotation speed of 20r/min for 10min at the temperature of 150, 200, 250, 300 and 350 degrees C. The rotating bending processes carried out with various conditions show that the grains in cross-section and longitudinal section of magnesium alloy tube were refined for all samples by the rotating bending process with rotation speed of 20r/min for different rotation numbers and temperatures. The rotating bending temperature shows a various effects on the mechanical properties. When the temperature was 200 degrees C, the highest strength as well as ductility was obtained.

关键字：rotating bending process;microstructure control;mechanical properties;metal tube

页面范围：1956-1960

是否译文：否